Regarding the bending of China 6A02 aluminum plate, in fact, the bending coefficient of China 6A02 aluminum plate is regular, generally 0.8 times the thickness of China 6A02 aluminum plate, such as 3mm, China 6A02 aluminum plate bending coefficient is 2.4, 5mm China 6A02 aluminum plate bending coefficient is 2.4, 5mm China 6A02 aluminum plate The bending coefficient of the plate is 4. If you use a knife, it is generally better to use a sharp knife. If the pressure is too high with a straight sword, the china 6A02 aluminum plate is prone to cracks.

Reasons for cracking when china 6A02 aluminum plate is bent 180 degrees

1. The bending side is parallel to the rolling direction of the china 6A02 aluminum plate, so it is easy to crack, so turn the bending direction 90 degrees.

2. The 180-degree bending angle is too much, which is greater than the minimum bending radius. Generally, the bending radius is 1.5 times the thickness of the plate.

3. Due to the material, some china 6A02 aluminum plate is an alloy, and its toughness is not as good as that of pure aluminum china 6A02 aluminum plate, and it is easy to crack.

4. The thickness of the plate is too thick, and the bending of 180 degrees exceeds the bending limit of the material.

The above is the bending problem of China 6A02 aluminum plate introduced by the manufacturer of China 6A02 aluminum plate. I hope my summary can help you.